| タイトル: | Effect of crystallization on drawdown force at capillary extrusion for polyethylene |
| 著者: | Seemork, Jiraporn
Itoh, Tomoki
Nobukawa, Shogo
Yamaguchi, Masayuki |
| キーワード: | Elongational Flow
Drawdown force
Polyethylene
Capillary extrusion
Crystallization |
| 発行日: | 2016-03-18 |
| 出版者: | 日本レオロジー学会 |
| 誌名: | 日本レオロジー学会誌 |
| 巻: | 44 |
| 号: | 1 |
| 開始ページ: | 23 |
| 終了ページ: | 27 |
| DOI: | 10.1678/rheology.44.23 |
| 抄録: | The effect of crystallization on the drawdown force, i.e., the force needed to stretch a molten polymer uniaxially, was studied using conventional polyethylene samples. It was found that the drawdown force of high-density polyethylene (HDPE) increases with increasing the die length. This is attributed to the rapid crystallization owing to the low density of entanglement couplings after passing through a long die. On the contrary, the die length has no/little influence on the drawdown force of linear low-density polyethylene (LLDPE), indicating that the molecular orientation applied in a long die is almost relaxed prior to the crystallization. Even for LLDPE, however, the drawdown force becomes sensitive to the die length by the addition of a small amount of HDPE, because the crystallization process is accelerated. |
| Rights: | Copyright (C) 2016 日本レオロジー学会. Jiraporn Seemork, Tomoki Itoh, Shogo Nobukawa, Masayuki Yamaguchi, 日本レオロジー学会誌, 44(1), 2016, 23-27. http://dx.doi.org/10.1678/rheology.44.23 |
| URI: | http://hdl.handle.net/10119/13786 |
| 資料タイプ: | publisher |
| 出現コレクション: | c10-1. 雑誌掲載論文 (Journal Articles)
|
このアイテムのファイル:
| ファイル |
記述 |
サイズ | 形式 |
|---|
| 22265.pdf | | 363Kb | Adobe PDF | 見る/開く |
|
当システムに保管されているアイテムはすべて著作権により保護されています。
|